Nonwovens are finding more and more applications requiring flame retardancy in areas that were once the sole domain of woven textiles; Nonwoven products are mainly manufactured using synthetic fibers such as polyolefin, polyester or nylon that represent highly flammable products. Polypropylene, in particular, burns very rapidly with a relatively low amount of smoke and without leaving a char residue because of its wholly aliphatic hydrocarbon structure. Its self ignition temperature is around 570 C and it presents a rapid decomposition rate compared with wood and other cellulosic materials.
The use of nonwovens manufactured with synthetic fibers can thus lead to an increased fire risk in many cases. This has to be taken into account even more nowadays since there is a trend to replace high cost materials by lower cost materials, for example polypropylene.
retardancy of nonwovens can be achieved in two ways: additive
(mechanically blending the FR chemistry with the polymer prior to extrusion)
and topical (coating the fiber or fabric with the FR chemistry). Additive types
are useful with thermoplastics, while topical treatments can be used with
thermoplastics, thermosets and natural fibers.
What are Flame Retardants and how do they Work?
There are several stages in the combustion process: heating, decomposition, ignition, flame spread and smoke generation. The combustion leads to the production of heat that is fed back and pyrolyzes the polymer, produces more fuel, and keeps the combustion process going. Flame retardants are chemicals that interfere in one or several of the steps in the combustion process. This is done in four distinct modes of action:
1. Reaction in the gas phase,
2. Reaction in the condensed phase,
3. Cooling effect and
4. Dilution effect.
flame-retardant additive for nonwovens must meet the following
There are several ways in which the combustion process can be retarded by physical action:
1. By formation of a protective layer. Under an external heat flux the additives can form a shield with a low thermal conductivity that can reduce the heat transfer from the heat source to the material.
2. By cooling. The
degradation reactions of the additive can play a part in the energy balance
of combustion. The additive can degrade endothermally, which cools down
the substrate to a temperature below that required for sustaining the
3. By dilution. The incorporation of inert substances (e.g. fillers such as talc or chalk) and additives that produce inert gases on decomposition dilutes the fuel in the solid and gaseous phases so that the lower ignition limit of the gas mixture is not exceeded.
The most significant chemical reactions interfering with the combustion process take place in the condensed and gas phases:
1. Reaction in condensed phase. Here two types of reaction can take place. Firstly, breakdown of the polymer can be accelerated by the flame retardant causing a pronounced flow of the polymer and, hence, its withdrawal from the sphere of influence of the flame, which breaks away. Secondly, the flame retardant can cause a layer of carbon (charring), a ceramic-like structure and/or a glass to be formed on the polymer surface.
2. Reaction in gas phase. The radical mechanism of the combustion process that takes place in the gas phase is interrupted by the flame retardant or its degradation products.
The fire retardant additive systems may be used alone or in association with other systems in polymeric materials to obtain a synergistic effect, i.e. the protective effect is higher than is assumed from the addition of the separate effects of each system.
Different Approaches for Flame Retardant Nonwovens
Most fibers are highly combustible (except high performance fibers) and the flammability of derived fabrics largely depends on the construction and density of the fabric. Several approaches can be used to enhance the fire behavior of fiber based fabrics used either alone or in blends with other fibers:
Retardant Fibers for Nonwovens
To make flame retarded fibers, several approaches can be considered:
Synthetic fibers are numerous and all of them require flame retardancy, appropriate to their chemical formulation. We will then focus on the most established and used fibers. They include polylactic acid (PLA), polyester, polyamide and polypropylene. All these fibers are used for making nonwovens.
The multifilaments were knitted and the flammability studied using cone calorimetry at an external heat flux of 35 kW/m. Depending on the clay loading, the peak value of RHR is decreased by up to 38 % demonstrating the improved fire performance of these PLA fibers. Formation of char is observed in the case of the nanocomposites suggesting a mechanism of condensed-phase.
Polyester fibers are the main synthetic fibers used in the industrial manufacturing sector and can be found in several areas of application. As polyester fibers are easily flammable, flame retardancy is a significant issue. Polypropylene (PP) is presently one of the fastest growing fibers for technical end-uses where high tensile strength coupled with low cost are essential features.
acceptable flame retardant for polypropylene, especially fiber-forming grades,
Applications of Flame Retardant Nonwovens
In order to ensure the safety of the public with regard to fire, standards, regulations and requirements in this field are continually discussed and modified. It is not easy to navigate the maze of testing methods and standards. In Europe, harmonization was initiated in the 1990s and is still progressing. The new regulations present new challenges to the flame retardancy industry. Examples of applications of FR nonwovens are reported below.
The field of protective garments is relatively large with differing requirements since it incorporates the protection of men at work and military applications, as well as clothing for firefighters. This problem is also relatively complex since a number of properties are required for a material to be used in this field of application. Indeed, heat protective performance is needed, but also heat-moisture transfer properties and comfort performance including lightness, for example, have to be taken into account, and usually a balance between the heat and moisture barrier has to be found. Usually, protective fabrics are multilayer clothing containing up to five or six layers. Fire protective clothing for firefighters consists of at least four layers: outer and inner shell, moisture barrier, and thermal liner. These layers are expected to provide adequate heat, flame, liquid, chemical and mechanical protection. Nonwovens composed of high performance fibers are typically used as thermal liners in protective garments.
Fire-blockers for Seat and Upholstery
Fire-blockers are usually highly fire resistant materials that are placed beneath the exterior cover fabric of furnishing and the first layer of cushioning materials in seats, mattresses and upholsteries. The bulky cushioning materials represent the major fuel source and therefore the greatest hazard potential. The fire-blocker acts as a barrier between the heat source (flame, cigarette, etc.) and the cushioning materials limiting fire growth and development. Fabric-like fire-blockers include woven and needle punched fabrics made from highly resistant textile fibers such as glass, Nomex, Kevlar, PBI, etc. Some of the fabric-like fire-blockers available are engineered textile products that use a combination of different fibers and fabric treatments. The first modern generation of fire-blockers was introduced by DuPont under the trade name VonarTM during the 1970s.
Another application of FR nonwovens is flexible insulation panels for building construction. Although traditional thermal insulation materials such as mineral wool or polystyrene are widely used, the return to ecology and nature noticed in several application fields is also observed in the building industry. Natural wool, coconut or even duck feathers are used to design thermal insulation panels. However, all these materials burn easily and thus FR treatments are required. The development of needle punched nonwovens and air-laid nonwovens based on fire retardant modified natural fibers has been reported and has been demonstrated that such materials meet the requirements for use in building applications. Finally, it is noteworthy that there are applications where FR properties are required in disposable nonwovens, for example for surgical drapes used in operating rooms as well as air filters used in the automotive industry.
This article was originally published in Textile learner blog run by Mazharul Islam Kiron.